GEOMEMBRANES POLYETHYLENE I HDPE Dimensional Properties Tensile Properties ASTM D 6693 [3] Strength Elongation Oxidative Induction Time (OIT) (min. avg.) [7] Oven Aging at 85ºC ASTM D 5721 [7], [8] Standard OIT High Pressure OIT UV Resistance GM 11 [9] Atarfil S.L. l www.atarfil.com GBM TMT HD EVO✧✧ (asperity height 0.7mm / 30mils) GMB TMT HD EVO✧✧ (asperity height 0.5mm / 20mils) GMB TMT HD EVO✧✧ (asperity height 0.5mm / 20mils) HDPE CX-T HDPE CX-T HDPE CX-T " W:6.0 (19.7) L: 131 (432) " " W: 6.0 / 6.3 / 7.5 (19.7 / 20.6 /24.6) L: 100 (328) " " W: 6.0 / 6.3 / 7.5 (19.7 / 20.6 /24.6) L: 80 (262) " 2.0 (80) ≥ 0.942 1.5 (60) ≥ 0.942 2.0 (80) ≥ 0.942 29 (168) 22 (126) 29 (168) 21 (120) 22 (125) 30 (171) > 13 ≥ 300 0.556 (125) 0.249 (56) > 13 ≥ 400 0.450 (101) 0.187 (42) > 13 ≥ 400 0.570 (128) 0.249 (56) High 2-2.5 1, 2 ≥3000✧ 120 500 55✧✧✧ 80✧✧✧ 75 demanding applications High 2-2.5 1, 2 ≥3000✧ 120 500 55✧✧✧ 80✧✧✧ 75 demanding applications High 2-2.5 1, 2 ≥3000✧ 120 500 55✧✧✧ 80✧✧✧ 75 demanding applications ✧Additional information regarding correlation between Test Methods ISO 18488 (Strain hardening) and ASTM D 5397 (Stress Crack Resistance) available upon request. Test conducted on representative smooth membrane samples. ✧✧Product can be manufactured with single (TM) or double (TMT) structured textured. ✧✧✧Product retained both Standard OIT (55%) and HP OIT (80%) after 90 days Oven Aging at 80 C ASTM D 5721 All Atarfil geomembranes are available in different thicknesses (from 0.75 to 4.00mm) and colors. Also an electrically conductive layer can be added upon request. HUITEX l www.huitex.com HUITEX Both OIT Series HUITEX Colored Series HUITEX K-Liner CPL series HDPE CX HDPE CX HDPE 7 (23) ~ 8 (26) / 70 (230) ~ 420 (1378) 7 (23) ~ 8 (26) / 70 (230) ~ 420 (1378) 2.5 (8.21) ~ 3.0 (9.75) / 60 (197) ~ 70 (230) 0.50 (20) ~ 3.00 (120) 0.50 (20) ~ 3.00 (120) 2.00 (80) ~ 5.00 (200) 0.940 0.940 (black layer) 0.940 7 (40) ~ 44 (252) 7 (40) ~ 44 (252) 30 (172) ~ 75 (430) 13 (74) ~ 80 (458) 13 (74) ~ 80 (458) 50 (287) ~ 125 (716) 12 100 ~ 700 12 500 0.16 (35) ~ 0.96 (211) 0.640 (141) ~ 1.60 (352) 12 100 ~ 700 0.16 (35) ~ 0.96 (211) 0.06 (14) ~ 0.37 (81) 0.06 (14) ~ 0.37 (81) 0.25 (55) ~ 0.63 (138) 2.0 ~ 3.0 2.0 ~ 3.0 black layer 2.0 ~ 3.0 cat.1/2 cat.1/2 black layer cat.1/2 500 100 500 100 black layer 500 100 400 400 black layer 400 55 55 black layer NA 80 80 black layer NA 50 50 black layer NA all all Concrete Protection [1] HDPE = High density polyethylene = Coextruded CX T = Textured S = Smooth [2] Lowest individual of 10 values [3] Machine direction (MD) and cross machine direction (XD) average values should be on the basis of 5 test specimens each direction * Yield elongation calculated with a gage length of 33mm * Break elongation calculated with a gage length of 50mm [4] Other methods such as D 4218 (muffle furnace) or microwave methods are acceptable if an appropriate correlation to D 1603 (tube furnace) can be established. [5] Carbon black dispersion for 10 different views: * minimum 9 of 10 in Categories 1 or 2 * all 10 in Categories 1, 2, or 3 [9] [6] The yield stress used to calculate the applied load for the SP-NCTL test should be the manufacturer's mean value via MQC testing. [7] The manufacturer has the option to select either one of the OIT methods listed to evaluate the antioxidant content in the geomembrane. [8] It also is recommended to evaluate samples at 30 and 60 days to compare with the 90 day response. The condition of the test should be 20 hr. UV cycle at 75 C followed by 4 hr. condensation at 60 C. [10] UV resistance is based on percent retained value regardless of the original HP-OIT value. [11] CL = Canal liner SIL = Surface impoundment liner SIC = Surface impoundment cover LL = Landfill liner DP = Decorative pond NP = Not provided by manufacturer NA = Not applicable, per manufacturer « Geosynthetics recommends you contact the manufacturers before making any specifying/purchasing decisions » 58 Geosynthetics | December 2022 January 2023 DL = Dam liner LPL = Leach pad liner LC = Landfill cover TL = Tunnel liner RP = Reserve pit Product Name Base Polymer [1] Roll Width/Length m (ft) Thickness ASTM D5199 (smooth) ASTM D5994 (textured) min. avg. mm (mils) [2] Density ASTM D1505/D792 (min.) (g/cm3 min.) Yield Stress kN/m (lb/in) Break Stress kN/m (lb/in) Yield Elongation % Break Elongation % Puncture Resistance D 4833 (min. avg.) kN (lb) Tear Resistance ASTM D 1004 (min. avg.) kN (lb) Carbon Black Content ASTM D 1603 range (%) [4] Carbon Black Dispersion ASTM D 5596 [5] Stress Crack Resistance ASTM D 5397 Appendix [6] Standard OIT ASTM D 3895 High Pressure OIT ASTM D 5885 ASTM D3895 % retained after 90 days ASTM D5885 % retained after 90 days High Pressure OIT (min. age.) % retained after 1600 hrs [10] Manufacturer's Suggested Applications [11]http://www.atarfil.com http://www.huitex.com