Geosynthetics December 2019/January 2020 - 69

GEOMEMBRANES

POLYETHYLENE I HDPE

Carbon Black Dispersion ASTM D 5596 [5]

Stress Crack Resistance ASTM D 5397 Appendix [6]

Standard OIT ASTM D 3895

High Pressure OIT ASTM D 5885

ASTM D3895 % retained after 90 days

ASTM D5885 % retained after 90 days

High Pressure OIT (min. age.)
% retained after 1600 hrs [10]

Manufacturer's Suggested Applications [11]

1.5 (60)

0.940

22
(126)

40
(228)

12

700

0.480 (108)

0.187
(42)

2-3

1, 2, 3

300

100

400

55

80

50

all

Solmax HDPE
Series Leak
Location Liner
Smooth

HDCX-S

6.86/131
(22.5/430)

2.0 (80)

0.940

29
(168)

53
(304)

12

700

0.640 (144)

0.249
(56)

2-3

1, 2, 3

300

100

400

55

80

50

all

Solmax HDPE
Series Leak
Location Liner
Textured

HDCX-T

6.86/158
(22.5/520)

1.5 (60)

0.940

22
(126)

16
(90)

12

100

0.400 (90)

0.187
(42)

2-3

1, 2, 3

300

100

400

55

80

50

all

Solmax HDPE
Series Leak
Location Liner
Textured

HDCX-T

6.86/122
(22.5/400)

2.0 (80)

0.940

29
(168)

21
(120)

12

100

0.534 (120)

0.249
(56)

2-3

1, 2, 3

300

100

400

55

80

50

all

Solmax HDPE
Series Smooth

HD-S

6.86/171
(22.5/560)

1.5 (60)

0.940

22
(126)

40
(228)

12

700

0.480 (108)

0.187
(42)

2-3

1, 2, 3

300

100

400

55

80

50

all

Solmax HDPE
Series Textured

HD-C-T

6.86/158
(22.5/520)

1.5 (60)

0.940

22
(126)

16
(90)

12

100

0.400 (90)

0.187
(42)

2-3

1, 2, 3

300

100

400

55

80

50

all

Solmax HighPerformance HD
Series Smooth

CX-S

6.86/171
(22.5/560)

1.5 (60)

0.940

23
(132)

42
(243)

13

800

0.556 (125)

0.187
(42)

2-3

1, 2, 3

1000

160

800

N/A

80

80

all

Solmax HighPerformance HD
Series Smooth

CX-S

6.86/131
(22.5/430)

2.0 (80)

0.940

31
(177)

57
(327)

13

800

0.711 (160)

0.257
(58)

2-3

1, 2, 3

1000

160

800

N/A

80

80

all

Solmax HighPerformance HD
Series Textured

CX-T

6.86/158
(22.5/520)

1.5 (60)

0.940

23
(132)

20
(115)

13

200

0.578 (130)

0.200
(45)

2-3

1, 2, 3

1000

160

800

N/A

80

80

all

Solmax HighPerformance HD
Series Textured

CX-T

6.86/122
(22.5/400)

2.0 (80)

0.940

31
(177)

27
(155)

13

200

0.711 (160)

0.266
(60)

2-3

1, 2, 3

1000

160

800

N/A

80

80

all

Solmax High
Temperature
Series Liner

HD-S

7.5/130
(24.6/427)

1.5 (60)

0.940

22
(126)

40
(228)

12

600

0.480 (108)

0.190
(43)

2-3

1, 2, 3

500

160

800

N/A

90

80

High
Temperature
Applications

Elongation

Break Stress kN/m (lb/in)

Strength

Yield Stress kN/m (lb/in)

Product Name

Density ASTM D1505/D792 (min.) (g/cm3 min.)

6.86/171
(22.5/560)

Thickness ASTM D5199 (smooth)
ASTM D5994 (textured) min. avg. mm
(mils) [2]

HDCX-S

Roll Width/Length m (ft)

Solmax HDPE
Series Leak
Location Liner
Smooth

Base Polymer [1]

Carbon Black Content ASTM D 1603 range (%) [4]

UV
Resistance
GM 11 [9]

Tear Resistance ASTM D 1004 (min. avg.) kN (lb)

Oven Aging at
85ºC ASTM D
5721 [7], [8]

Puncture Resistance D 4833 (min. avg.) kN (lb)

Oxidative
Induction
Time (OIT)
(min. avg.)
[7]

Break Elongation %

Tensile Properties
ASTM D 6693 [3]

Yield Elongation %

Dimensional
Properties

High
Standard
Pressure
OIT
OIT

Solmax International Inc. l www.solmax.com

Note: All of Solmax Geomembranes are available in a variety of thicknesses and with black, white or green surface layers.

[1]	
	
[2]	
[3]	
	
	
	
	
[4]	
	
	

HDPE	 = High density polyethylene	
T	 = Textured
CX	
= Coextruded	
S	 = Smooth
Lowest individual of 10 values
Machine direction (MD) and cross machine direction (XD)
average values should be on the basis of 5 test specimens
each direction
* Yield elongation calculated with a gage length of 33mm
* Break elongation calculated with a gage length of 50mm
Other methods such as D 4218 (muffle furnace) or
microwave methods are acceptable if an appropriate
correlation to D 1603 (tube furnace) can be established.

[5]	
	
	
[6]	
	
	
[7]	
	
[8]	
	

Carbon black dispersion for 10 different views:
* minimum 9 of 10 in Categories 1 or 2
* all 10 in Categories 1, 2, or 3
The yield stress used to calculate the applied load for the
SP-NCTL test should be the manufacturer's mean value
via MQC testing.
The manufacturer has the option to select either one of the OIT
methods listed to evaluate the antioxidant content in the geomembrane.
It also is recommended to evaluate samples at 30 and 60 	
days to compare with the 90 day response.

[9]	 The condition of the test should be 20 hr. UV cycle at
	
75 C followed by 4 hr. condensation at 60 C.
[10] UV resistance is based on percent retained value
	
regardless of the original HP-OIT value.
[11]	 CL	 = Canal liner	
DL	
	
SIL	 = Surface impoundment liner	
LPL	
	
SIC	 = Surface impoundment cover	
LC	
	
LL	 = Landfill liner	
TL	
	
DP	 = Decorative pond	
RP	
	
NP	 = Not provided by manufacturer
	
NA	 = Not applicable, per manufacturer

= Dam liner
= Leach pad liner
= Landfill cover
= Tunnel liner
= Reserve pit

« Geosynthetics recommends you contact the manufacturers before making any specifying/purchasing decisions »
www.GeosyntheticsMagazine.com

69
http://www.solmax.com http://www.GeosyntheticsMagazine.com