Geosynthetics December 2019/January 2020 - 92

GEOGRIDS
Tensile Strength/[Elongation]
ASTM D 6637 [2] kN/m (lb/ft)/%

MD

XD

MD

XD

Creep Limited
Strength-MD [3]
ASTM D 5262 kN/m (lb/ft)

LTDS GRI GG4-MD [4]
kN/m (lb/ft) (in sand)

Manufacturer's
Suggested
Applications [5]

NA

NA

25 [A] (1.0) [A]

33 [A] (1.3) [A]

11.8 (810)

19.6 (1340)

19.2 (1310)

28.8 (1970)

NA

NA

SI, B

TX130S

Integrally formed

PP

NA

NA

NA

NA

NA

NA

NA

NA

NA

NA

SI, B

TX160

Integrally formed

PP

NA

NA

NA

NA

NA

NA

NA

NA

NA

NA

SI, B

TX5

Integrally formed

PP

NA

NA

NA

NA

NA

NA

NA

NA

NA

NA

SI, B

TX7

Integrally formed

PP

NA

NA

NA

NA

NA

NA

NA

NA

NA

NA

SI, B

TX190L

Integrally formed

PP

NA

NA

NA

NA

NA

NA

NA

NA

NA

NA

SI, B

Knitted

FG

EP

405 (12)

25 (1.0)

25 (1.0)

NA

NA

100 @ 3%
(6720)

100 @ 3%
(6720)

NA

NP

A/O, PR

Knitted w/
tackﬁlm (TF)

FG TF

EP

432 (12.7)

25 (1.0)

25 (1.0)

NA

NA

100 @ 3%
(6720)

100 @ 3%
(6720)

NA

NP

A/O, PR

21.2 (1450)✧

W, E, S

Aperture Size
mm (in)

MD

Coating Type [1]

Mass/Unit Area
ASTM D 5261 g/m2
(oz/yd2)

PP

Polymer Type [1]

Integrally formed

Manufacturing Process

BX1200 (BX Class 2)

Product Name

XD

Dimensional Properties [2]

Strength @ 5% Strain

Ultimate Strength/%
(Tult)

Tensar International Corp. l www.tensar-international.com

GlasGrid 8511
GlasGrid 8511TF
UX1100HS/MSE✧✧

Integrally formed

HDPE

NA

NA

430 (17.0)

NA

27 (1850)

NA

58 (3970)

NA

22.3 (1530)✧

UX1400HS/MSE✧✧

Integrally formed

HDPE

NA

NA

460 (18.0)

NA

31 (2130)

NA

70 (4800)

NA

26.9 (1850)✧

25.6 (1760)✧

W, E, S

UX1500HS/MSE✧✧

Integrally formed

HDPE

NA

NA

460 (18.0)

NA

52 (3560)

NA

114 (7810)

NA

43.8 (3000)✧

41.8 (2860)✧

W, E, S

UX1600HS/MSE✧✧

Integrally formed

HDPE

NA

NA

460 (18.0)

NA

58 (3980)

NA

144 (9870)

NA

55.4 (3800)✧

52.7 (3620)✧

W, E, S

UX1700HS/MSE✧✧

Integrally formed

HDPE

NA

NA

460 (18.0)

NA

75 (5140)

NA

175 (11,990)

NA

67.3 (4610)✧

64.1 (4390)✧

W, E, S

230 (15,760)

NA

92.7 (6354)✧

88.3 (6050)✧

W, E, S

UX1900HS

Integrally formed

HDPE

NA

NA

420 (16.5)

NA

110 (7535)

NA

✧Creep rupture extrapolated to a 120-year time period per ASTM D 5262
✧✧UXxx00HS geogrids use for non-connected system only

Thrace-LINQ Inc. l www.thracelinq.com
TLG-11 ( type 1 )

Integrally formed

PP

NA

NA

25 (1.0)

33 (1.3)

9.5 (651)

14.0 (960)

12.6 (863)

19.2 (1316)

NA

NA

SI, B

TLG-12 ( type 2 )

Integrally formed

PP

NA

NA

25 (1.0)

33 (1.3)

13.0 (891)

21.0 (1439)

19.5 (1336)

30.0 (2056)

NA

NA

SI, B

Titan Environmental Containment Ltd. l www.titanenviro.com
TE-FGP21
Fiberglass Grid

Woven

FG

Polymeric

610 (18.1)

25.4 (1.0)

19.0 (0.75)

NA

NA

100 (6854)

200 (13,708)

NA

NA

A/O, PR

TE-FGP10
Fiberglass Grid

Woven

FG

Polymeric

420 (12.5)

12.7 (0.5)

12.7 (0.5)

NA

NA

100 (6854)

100 (6854)

NA

NA

A/O, PR

TE-FGP11
Fiberglass Grid

Woven

FG

Polymeric

420 (12.5)

25.4 (1.0)

25.4 (1.0)

NA

NA

100 (6854)

100 (6854)

NA

NA

A/O, PR

TE-FGP20
Fiberglass Grid

Woven

FG

Polymeric

610 (18.1)

12.7 (0.5)

12.7 (0.5)

NA

NA

100 ( 6854)

200 (13,708)

NA

NA

A/O, PR

TE-FGC10
Composite Grid

Woven

FG PP

Polymeric

570 (16.9)

12.7 (0.5)

12.7 (0.5)

NA

NA

100 (6854)

100 (6854)

NA

NA

A/O, PR

[1]	
	
	
	
	
	
[2]	
	
[3]	
	

PET	 = Polyester, HDPE = High density polyethylene
PVC	 = Polyvinyl chloride
EP	 = Elastomeric Polymer
PVA	 = Polyvinyl alcohol
FG	 = Fiberglass
PP	 = Polypropylene
MD	 = Machine direction
XD	 = Cross-machine direction
Test per ASTM D 5262, for a minimum of 10,000 hours
and extrapolate to a 75-year time period.

[4]	 LTDS =

	RFCR = Reduction factor for creep
	RFID = Reduction factor for installation damage
	RFD = Reduction factor for durability

[5]	
	
	
	
	
	
	

NOTE: this equation does not include other reduction factors
that may apply to design. Reduction factors are site specific
and should be reviewed on a per project basis. Contact the
manufacturer for recommendations.

NP	 = Not provided by manufacturer
NA	 = Not applicable, per manufacturer
* = Not for sale in U.S.

	

Tult
RFCR x RFID x RFD

A/O	
B	
E	
PR	
S	
SI	
W	

= Asphalt overlay
= Base reinforcement
= Embankments
= Pavement reinforcement
= Slopes
= Subgrade improvement
= Walls

Companies were
requested to provide
minimum average
roll values (MARV).
All claims are the
responsibility of the
manufacturer.

« Geosynthetics recommends you contact the manufacturers before making any specifying/purchasing decisions »

92

Geosynthetics | December 2019 January 2020
http://www.tensar-international.com http://www.thracelinq.com http://www.titanenviro.com
Geosynthetics December 2019/January 2020

Table of Contents for the Digital Edition of Geosynthetics December 2019/January 2020