PORCELAIN NORITAKE Universal Paste Opaque Features 1. Universal Paste Opaque can be used for a wide range of alloys such as High Noble, Noble, Co-Cr and Ni-Cr alloys. 2. Universal Paste Opaque has a very good bonding characteristic with alloys and is very easy to use. 3. A wide variety of 22 shades including Noritake Original Shades and Esthetic Shades are available. Baking Schedule Using High Noble, Noble, Ni-Cr alloys with beryllium 1st and 2nd bake 8min. Low Temperature Start Vacuum Heat Rate Vacuum Level Released Vacuum High Temperature Hold Time Cool Time 9800 9800 C C 1min. (air) 0min. C (7520 F) in order to avoid bubble problems. 4000 4000 650 C C C/min. 96kpa * 17960 17960 F F 10000 10000 C C 1min. (air) 0min. Note: The above program is only a guideline, Baking temperature may be varied with the peculiarities of different furnaces Set the idle temperature of the furnace under 4000 *96kPa = 72cmHg (29 inchesHg) SHOP NOW! 448 To order, visit: www.zahndental.com 7520 7520 1170 F F F/min. 4000 4000 650 C C C/min. 96kpa * 18320 18320 F F Using High Nobel, Nobel, Ni-Cr alloys with beryllium 1st and 2nd bake Dry-Out Time Using Ni-Cr alloys without beryllium and Co-Cr alloys 1st and 2nd bake 8min. 7520 7520 1170 F F F/min. 21ZC7813http://www.zahndental.com